MakeItFrom.com
Menu (ESC)

S31803 Stainless Steel vs. EN 1.0580 Steel

Both S31803 stainless steel and EN 1.0580 steel are iron alloys. They have 69% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is S31803 stainless steel and the bottom bar is EN 1.0580 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 260
160 to 180
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 29
5.6 to 25
Fatigue Strength, MPa 370
210 to 270
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 80
73
Shear Strength, MPa 460
340 to 360
Tensile Strength: Ultimate (UTS), MPa 710
540 to 620
Tensile Strength: Yield (Proof), MPa 500
290 to 450

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1060
400
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 16
51
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 17
1.8
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.6
1.4
Embodied Energy, MJ/kg 49
18
Embodied Water, L/kg 160
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
31 to 120
Resilience: Unit (Modulus of Resilience), kJ/m3 630
230 to 540
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 25
19 to 22
Strength to Weight: Bending, points 23
19 to 21
Thermal Diffusivity, mm2/s 4.3
14
Thermal Shock Resistance, points 20
17 to 20

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.22
Chromium (Cr), % 21 to 23
0
Iron (Fe), % 63.7 to 71.9
97.5 to 100
Manganese (Mn), % 0 to 2.0
0 to 1.6
Molybdenum (Mo), % 2.5 to 3.5
0
Nickel (Ni), % 4.5 to 6.5
0
Nitrogen (N), % 0.080 to 0.2
0
Phosphorus (P), % 0 to 0.030
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 0.55
Sulfur (S), % 0 to 0.020
0 to 0.045