S32003 Stainless Steel vs. SAE-AISI M44 Steel

Both S32003 stainless steel and SAE-AISI M44 steel are iron alloys. They have 75% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is S32003 stainless steel and the bottom bar is SAE-AISI M44 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 79
78
Tensile Strength: Ultimate (UTS), MPa 730
870 to 2290

Thermal Properties

Latent Heat of Fusion, J/g 290
270
Melting Completion (Liquidus), °C 1440
1590
Melting Onset (Solidus), °C 1400
1540
Specific Heat Capacity, J/kg-K 480
440
Thermal Conductivity, W/m-K 15
14
Thermal Expansion, µm/m-K 13
12

Otherwise Unclassified Properties

Base Metal Price, % relative 14
43
Density, g/cm3 7.8
8.4
Embodied Carbon, kg CO2/kg material 3.0
9.9
Embodied Energy, MJ/kg 42
150
Embodied Water, L/kg 150
170

Common Calculations

PREN (Pitting Resistance) 29
35
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 26
28 to 75
Strength to Weight: Bending, points 23
24 to 46
Thermal Diffusivity, mm2/s 4.0
3.7
Thermal Shock Resistance, points 21
27 to 70

Alloy Composition

Carbon (C), % 0 to 0.030
1.1 to 1.2
Chromium (Cr), % 19.5 to 22.5
4.0 to 4.8
Cobalt (Co), % 0
11 to 12.3
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 68.2 to 75.9
65.3 to 70.6
Manganese (Mn), % 0 to 2.0
0.2 to 0.4
Molybdenum (Mo), % 1.5 to 2.0
6.0 to 7.0
Nickel (Ni), % 3.0 to 4.0
0 to 0.3
Nitrogen (N), % 0.14 to 0.2
0
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0 to 1.0
0.3 to 0.55
Sulfur (S), % 0 to 0.020
0 to 0.030
Tungsten (W), % 0
5.0 to 5.8
Vanadium (V), % 0
1.9 to 2.2