S32050 Stainless Steel vs. CC334G Bronze

S32050 stainless steel belongs to the iron alloys classification, while CC334G bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is S32050 stainless steel and the bottom bar is CC334G bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
210
Elastic (Young's, Tensile) Modulus, GPa 210
120
Elongation at Break, % 46
5.6
Poisson's Ratio 0.28
0.33
Shear Modulus, GPa 81
45
Tensile Strength: Ultimate (UTS), MPa 770
810
Tensile Strength: Yield (Proof), MPa 370
410

Thermal Properties

Latent Heat of Fusion, J/g 310
240
Maximum Temperature: Mechanical, °C 1100
240
Melting Completion (Liquidus), °C 1460
1080
Melting Onset (Solidus), °C 1410
1020
Specific Heat Capacity, J/kg-K 470
450
Thermal Conductivity, W/m-K 12
41
Thermal Expansion, µm/m-K 16
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.9
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.1
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 31
29
Density, g/cm3 8.0
8.2
Embodied Carbon, kg CO2/kg material 6.0
3.6
Embodied Energy, MJ/kg 81
59
Embodied Water, L/kg 210
390

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 290
38
Resilience: Unit (Modulus of Resilience), kJ/m3 330
710
Stiffness to Weight: Axial, points 14
8.1
Stiffness to Weight: Bending, points 25
20
Strength to Weight: Axial, points 27
28
Strength to Weight: Bending, points 23
24
Thermal Diffusivity, mm2/s 3.3
11
Thermal Shock Resistance, points 17
28

Alloy Composition

Aluminum (Al), % 0
10 to 12
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 22 to 24
0
Copper (Cu), % 0 to 0.4
72 to 84.5
Iron (Fe), % 43.1 to 51.8
3.0 to 7.0
Lead (Pb), % 0
0 to 0.050
Magnesium (Mg), % 0
0 to 0.050
Manganese (Mn), % 0 to 1.5
0 to 2.5
Molybdenum (Mo), % 6.0 to 6.6
0
Nickel (Ni), % 20 to 23
4.0 to 7.5
Nitrogen (N), % 0.21 to 0.32
0
Phosphorus (P), % 0 to 0.035
0
Silicon (Si), % 0 to 1.0
0 to 0.1
Sulfur (S), % 0 to 0.020
0
Tin (Sn), % 0
0 to 0.2
Zinc (Zn), % 0
0 to 0.5