S32101 Stainless Steel vs. EN 1.0254 Steel

Both S32101 stainless steel and EN 1.0254 steel are iron alloys. They have 72% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is S32101 stainless steel and the bottom bar is EN 1.0254 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 260
120
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
27
Fatigue Strength, MPa 400
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
73
Shear Strength, MPa 490
280
Tensile Strength: Ultimate (UTS), MPa 740
430
Tensile Strength: Yield (Proof), MPa 500
250

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 1000
400
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1370
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
50
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 12
2.1
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 2.6
1.5
Embodied Energy, MJ/kg 38
19
Embodied Water, L/kg 150
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 230
100
Resilience: Unit (Modulus of Resilience), kJ/m3 640
170
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 27
15
Strength to Weight: Bending, points 24
16
Thermal Diffusivity, mm2/s 4.0
13
Thermal Shock Resistance, points 20
14

Alloy Composition

Carbon (C), % 0 to 0.040
0 to 0.16
Chromium (Cr), % 21 to 22
0 to 0.3
Copper (Cu), % 0.1 to 0.8
0 to 0.3
Iron (Fe), % 67.3 to 73.3
97.2 to 100
Manganese (Mn), % 4.0 to 6.0
0 to 1.2
Molybdenum (Mo), % 0.1 to 0.8
0 to 0.080
Nickel (Ni), % 1.4 to 1.7
0 to 0.3
Niobium (Nb), % 0
0 to 0.010
Nitrogen (N), % 0.2 to 0.25
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.35
Sulfur (S), % 0 to 0.030
0 to 0.020
Titanium (Ti), % 0
0 to 0.040
Vanadium (V), % 0
0 to 0.020