S32202 Stainless Steel vs. S35140 Stainless Steel

Both S32202 stainless steel and S35140 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 73% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is S32202 stainless steel and the bottom bar is S35140 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 250
210
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
34
Fatigue Strength, MPa 400
250
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 79
78
Shear Strength, MPa 490
460
Tensile Strength: Ultimate (UTS), MPa 730
690
Tensile Strength: Yield (Proof), MPa 510
310

Thermal Properties

Latent Heat of Fusion, J/g 290
300
Maximum Temperature: Corrosion, °C 440
500
Maximum Temperature: Mechanical, °C 1030
1100
Melting Completion (Liquidus), °C 1430
1420
Melting Onset (Solidus), °C 1380
1370
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
14
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 12
31
Density, g/cm3 7.7
8.0
Embodied Carbon, kg CO2/kg material 2.6
5.5
Embodied Energy, MJ/kg 37
78
Embodied Water, L/kg 150
190

Common Calculations

PREN (Pitting Resistance) 27
28
Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
190
Resilience: Unit (Modulus of Resilience), kJ/m3 650
250
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 27
24
Strength to Weight: Bending, points 24
22
Thermal Diffusivity, mm2/s 4.0
3.7
Thermal Shock Resistance, points 20
16

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.1
Chromium (Cr), % 21.5 to 24
20 to 22
Iron (Fe), % 69.4 to 77.3
44.1 to 52.7
Manganese (Mn), % 0 to 2.0
1.0 to 3.0
Molybdenum (Mo), % 0 to 0.45
1.0 to 2.0
Nickel (Ni), % 1.0 to 2.8
25 to 27
Niobium (Nb), % 0
0.25 to 0.75
Nitrogen (N), % 0.18 to 0.26
0.080 to 0.2
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 0.75
Sulfur (S), % 0 to 0.010
0 to 0.030