S32304 Stainless Steel vs. SAE-AISI 8617 Steel

Both S32304 stainless steel and SAE-AISI 8617 steel are iron alloys. Both are furnished in the annealed condition. They have 73% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is S32304 stainless steel and the bottom bar is SAE-AISI 8617 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 250
140
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 28
25
Fatigue Strength, MPa 330
230
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 79
73
Shear Strength, MPa 440
300
Tensile Strength: Ultimate (UTS), MPa 670
470
Tensile Strength: Yield (Proof), MPa 460
320

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 1050
410
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1380
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
43
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 14
2.6
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.8
1.5
Embodied Energy, MJ/kg 40
20
Embodied Water, L/kg 160
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
110
Resilience: Unit (Modulus of Resilience), kJ/m3 520
270
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 24
17
Strength to Weight: Bending, points 22
17
Thermal Diffusivity, mm2/s 4.0
12
Thermal Shock Resistance, points 18
15

Alloy Composition

Carbon (C), % 0 to 0.030
0.15 to 0.2
Chromium (Cr), % 21.5 to 24.5
0.4 to 0.6
Copper (Cu), % 0.050 to 0.6
0
Iron (Fe), % 65 to 75.4
96.9 to 98.1
Manganese (Mn), % 0 to 2.5
0.7 to 0.9
Molybdenum (Mo), % 0.050 to 0.6
0.15 to 0.25
Nickel (Ni), % 3.0 to 5.5
0.4 to 0.7
Nitrogen (N), % 0.050 to 0.2
0
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 1.0
0.15 to 0.35
Sulfur (S), % 0 to 0.030
0 to 0.040