S32550 Stainless Steel vs. EN 1.4828 Stainless Steel

Both S32550 stainless steel and EN 1.4828 stainless steel are iron alloys. They have 89% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is S32550 stainless steel and the bottom bar is EN 1.4828 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 260
190
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 21
33
Fatigue Strength, MPa 400
200
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 80
77
Shear Strength, MPa 540
430
Tensile Strength: Ultimate (UTS), MPa 860
650
Tensile Strength: Yield (Proof), MPa 620
260

Thermal Properties

Latent Heat of Fusion, J/g 300
320
Maximum Temperature: Corrosion, °C 450
420
Maximum Temperature: Mechanical, °C 1100
1000
Melting Completion (Liquidus), °C 1440
1400
Melting Onset (Solidus), °C 1390
1360
Specific Heat Capacity, J/kg-K 480
490
Thermal Conductivity, W/m-K 16
15
Thermal Expansion, µm/m-K 13
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 20
17
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 3.8
3.4
Embodied Energy, MJ/kg 53
48
Embodied Water, L/kg 180
150

Common Calculations

PREN (Pitting Resistance) 40
21
Resilience: Ultimate (Unit Rupture Work), MJ/m3 160
170
Resilience: Unit (Modulus of Resilience), kJ/m3 940
170
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 31
23
Strength to Weight: Bending, points 26
22
Thermal Diffusivity, mm2/s 4.4
4.0
Thermal Shock Resistance, points 23
14

Alloy Composition

Carbon (C), % 0 to 0.040
0 to 0.2
Chromium (Cr), % 24 to 27
19 to 21
Copper (Cu), % 1.5 to 2.5
0
Iron (Fe), % 57.2 to 67
61.1 to 68.5
Manganese (Mn), % 0 to 1.5
0 to 2.0
Molybdenum (Mo), % 2.9 to 3.9
0
Nickel (Ni), % 4.5 to 6.5
11 to 13
Nitrogen (N), % 0.1 to 0.25
0 to 0.1
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 1.0
1.5 to 2.5
Sulfur (S), % 0 to 0.030
0 to 0.015