S32654 Stainless Steel vs. AWS E316H
Both S32654 stainless steel and AWS E316H are iron alloys. They have 77% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is S32654 stainless steel and the bottom bar is AWS E316H.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 200 |
| Elongation at Break, % | 45 | |
| 34 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 82 | |
| 78 |
| Tensile Strength: Ultimate (UTS), MPa | 850 | |
| 580 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 290 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1440 |
| Melting Onset (Solidus), °C | 1410 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 470 |
| Thermal Conductivity, W/m-K | 11 | |
| 15 |
| Thermal Expansion, µm/m-K | 15 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
| 2.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.5 | |
| 2.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 34 | |
| 20 |
| Density, g/cm3 | 8.0 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 6.4 | |
| 4.0 |
| Embodied Energy, MJ/kg | 87 | |
| 55 |
| Embodied Water, L/kg | 220 | |
| 160 |
Common Calculations
| PREN (Pitting Resistance) | 57 | |
| 27 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 29 | |
| 21 |
| Strength to Weight: Bending, points | 25 | |
| 20 |
| Thermal Diffusivity, mm2/s | 2.9 | |
| 4.0 |
| Thermal Shock Resistance, points | 19 | |
| 15 |
Alloy Composition
| Carbon (C), % | 0 to 0.020 | |
| 0.040 to 0.080 |
| Chromium (Cr), % | 24 to 25 | |
| 17 to 20 |
| Copper (Cu), % | 0.3 to 0.6 | |
| 0 to 0.75 |
| Iron (Fe), % | 38.3 to 45.3 | |
| 58.6 to 69.5 |
| Manganese (Mn), % | 2.0 to 4.0 | |
| 0.5 to 2.5 |
| Molybdenum (Mo), % | 7.0 to 8.0 | |
| 2.0 to 3.0 |
| Nickel (Ni), % | 21 to 23 | |
| 11 to 14 |
| Nitrogen (N), % | 0.45 to 0.55 | |
| 0 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.0050 | |
| 0 to 0.030 |