S32750 Stainless Steel vs. EN 1.0237 Steel

Both S32750 stainless steel and EN 1.0237 steel are iron alloys. They have 63% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is S32750 stainless steel and the bottom bar is EN 1.0237 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 270
140
Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 17
20
Fatigue Strength, MPa 360
250
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 81
73
Shear Strength, MPa 530
290
Tensile Strength: Ultimate (UTS), MPa 860
470
Tensile Strength: Yield (Proof), MPa 590
360

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
52
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 21
1.8
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 4.1
1.4
Embodied Energy, MJ/kg 56
18
Embodied Water, L/kg 180
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 130
88
Resilience: Unit (Modulus of Resilience), kJ/m3 860
340
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 31
17
Strength to Weight: Bending, points 26
17
Thermal Diffusivity, mm2/s 4.0
14
Thermal Shock Resistance, points 25
15

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.2
Chromium (Cr), % 24 to 26
0
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 58.1 to 66.8
98 to 100
Manganese (Mn), % 0 to 1.2
0 to 1.4
Molybdenum (Mo), % 3.0 to 5.0
0
Nickel (Ni), % 6.0 to 8.0
0
Nitrogen (N), % 0.24 to 0.32
0
Phosphorus (P), % 0 to 0.035
0 to 0.045
Silicon (Si), % 0 to 0.8
0 to 0.35
Sulfur (S), % 0 to 0.020
0 to 0.045