S32760 Stainless Steel vs. AISI 304Cu Stainless Steel

Both S32760 stainless steel and AISI 304Cu stainless steel are iron alloys. Both are furnished in the annealed condition. They have 88% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is S32760 stainless steel and the bottom bar is AISI 304Cu stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 250
160
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 28
45
Fatigue Strength, MPa 450
190
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 80
76
Shear Strength, MPa 550
370
Tensile Strength: Ultimate (UTS), MPa 850
530
Tensile Strength: Yield (Proof), MPa 620
210

Thermal Properties

Latent Heat of Fusion, J/g 300
290
Maximum Temperature: Corrosion, °C 450
420
Maximum Temperature: Mechanical, °C 1100
930
Melting Completion (Liquidus), °C 1460
1410
Melting Onset (Solidus), °C 1410
1370
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 15
13
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
2.8

Otherwise Unclassified Properties

Base Metal Price, % relative 22
16
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 4.1
3.0
Embodied Energy, MJ/kg 57
43
Embodied Water, L/kg 180
150

Common Calculations

PREN (Pitting Resistance) 42
18
Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
190
Resilience: Unit (Modulus of Resilience), kJ/m3 930
110
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 30
19
Strength to Weight: Bending, points 25
19
Thermal Diffusivity, mm2/s 4.0
3.5
Thermal Shock Resistance, points 23
12

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 24 to 26
17 to 19
Copper (Cu), % 0.5 to 1.0
3.0 to 4.0
Iron (Fe), % 57.6 to 65.8
63.9 to 72
Manganese (Mn), % 0 to 1.0
0 to 2.0
Molybdenum (Mo), % 3.0 to 4.0
0
Nickel (Ni), % 6.0 to 8.0
8.0 to 10
Nitrogen (N), % 0.2 to 0.3
0
Phosphorus (P), % 0 to 0.030
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.010
0 to 0.030
Tungsten (W), % 0.5 to 1.0
0