S32906 Stainless Steel vs. EN 1.3536 Steel

Both S32906 stainless steel and EN 1.3536 steel are iron alloys. They have 63% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is S32906 stainless steel and the bottom bar is EN 1.3536 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 270
200
Elastic (Young's, Tensile) Modulus, GPa 210
190
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 81
73
Tensile Strength: Ultimate (UTS), MPa 850
660

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1100
440
Melting Completion (Liquidus), °C 1430
1450
Melting Onset (Solidus), °C 1380
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 13
41
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 20
2.9
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 3.7
1.6
Embodied Energy, MJ/kg 52
21
Embodied Water, L/kg 190
55

Common Calculations

PREN (Pitting Resistance) 41
2.8
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 30
23
Strength to Weight: Bending, points 26
22
Thermal Diffusivity, mm2/s 3.6
11
Thermal Shock Resistance, points 23
19

Alloy Composition

Aluminum (Al), % 0
0 to 0.050
Carbon (C), % 0 to 0.030
0.93 to 1.1
Chromium (Cr), % 28 to 30
1.7 to 2.0
Copper (Cu), % 0 to 0.8
0 to 0.3
Iron (Fe), % 56.6 to 63.6
96 to 97.4
Manganese (Mn), % 0.8 to 1.5
0.6 to 0.8
Molybdenum (Mo), % 1.5 to 2.6
0.2 to 0.35
Nickel (Ni), % 5.8 to 7.5
0
Nitrogen (N), % 0.3 to 0.4
0
Oxygen (O), % 0
0 to 0.0015
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0 to 0.5
0.15 to 0.45
Sulfur (S), % 0 to 0.030
0 to 0.030