S32950 Stainless Steel vs. ASTM A372 Grade A Steel

Both S32950 stainless steel and ASTM A372 grade A steel are iron alloys. They have 66% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is S32950 stainless steel and the bottom bar is ASTM A372 grade A steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 260
140
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 17
22
Fatigue Strength, MPa 330
190
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 80
73
Shear Strength, MPa 480
320
Tensile Strength: Ultimate (UTS), MPa 780
500
Tensile Strength: Yield (Proof), MPa 550
270

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1430
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 16
52
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 17
1.8
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 3.4
1.4
Embodied Energy, MJ/kg 47
18
Embodied Water, L/kg 180
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
95
Resilience: Unit (Modulus of Resilience), kJ/m3 730
200
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 28
18
Strength to Weight: Bending, points 24
18
Thermal Diffusivity, mm2/s 4.3
14
Thermal Shock Resistance, points 21
16

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.3
Chromium (Cr), % 26 to 29
0
Iron (Fe), % 60.3 to 69.4
98.3 to 99.85
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 1.0 to 2.5
0
Nickel (Ni), % 3.5 to 5.2
0
Nitrogen (N), % 0.15 to 0.35
0
Phosphorus (P), % 0 to 0.035
0 to 0.015
Silicon (Si), % 0 to 0.6
0.15 to 0.35
Sulfur (S), % 0 to 0.010
0 to 0.010