S33228 Stainless Steel vs. 5652 Aluminum
S33228 stainless steel belongs to the iron alloys classification, while 5652 aluminum belongs to the aluminum alloys. There are 27 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is S33228 stainless steel and the bottom bar is 5652 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 190 | |
| 47 to 77 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 68 |
| Elongation at Break, % | 34 | |
| 6.8 to 25 |
| Fatigue Strength, MPa | 170 | |
| 60 to 140 |
| Poisson's Ratio | 0.28 | |
| 0.33 |
| Shear Modulus, GPa | 79 | |
| 26 |
| Shear Strength, MPa | 380 | |
| 110 to 170 |
| Tensile Strength: Ultimate (UTS), MPa | 570 | |
| 190 to 290 |
| Tensile Strength: Yield (Proof), MPa | 210 | |
| 74 to 260 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 1100 | |
| 190 |
| Melting Completion (Liquidus), °C | 1410 | |
| 650 |
| Melting Onset (Solidus), °C | 1360 | |
| 610 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 900 |
| Thermal Expansion, µm/m-K | 16 | |
| 24 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 37 | |
| 9.5 |
| Density, g/cm3 | 8.0 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 6.2 | |
| 8.6 |
| Embodied Energy, MJ/kg | 89 | |
| 150 |
| Embodied Water, L/kg | 220 | |
| 1190 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 150 | |
| 12 to 39 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 110 | |
| 40 to 480 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 51 |
| Strength to Weight: Axial, points | 20 | |
| 20 to 30 |
| Strength to Weight: Bending, points | 19 | |
| 27 to 36 |
| Thermal Shock Resistance, points | 13 | |
| 8.4 to 13 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.025 | |
| 95.8 to 97.7 |
| Carbon (C), % | 0.040 to 0.080 | |
| 0 |
| Cerium (Ce), % | 0.050 to 0.1 | |
| 0 |
| Chromium (Cr), % | 26 to 28 | |
| 0.15 to 0.35 |
| Copper (Cu), % | 0 | |
| 0 to 0.040 |
| Iron (Fe), % | 36.5 to 42.3 | |
| 0 to 0.4 |
| Magnesium (Mg), % | 0 | |
| 2.2 to 2.8 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 0.010 |
| Nickel (Ni), % | 31 to 33 | |
| 0 |
| Niobium (Nb), % | 0.6 to 1.0 | |
| 0 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 |
| Silicon (Si), % | 0 to 0.3 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 0.1 |
| Residuals, % | 0 | |
| 0 to 0.15 |