S33228 Stainless Steel vs. ACI-ASTM CD6MN Steel
Both S33228 stainless steel and ACI-ASTM CD6MN steel are iron alloys. They have 71% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is S33228 stainless steel and the bottom bar is ACI-ASTM CD6MN steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 200 |
| Elongation at Break, % | 34 | |
| 28 |
| Fatigue Strength, MPa | 170 | |
| 370 |
| Poisson's Ratio | 0.28 | |
| 0.27 |
| Shear Modulus, GPa | 79 | |
| 80 |
| Tensile Strength: Ultimate (UTS), MPa | 570 | |
| 730 |
| Tensile Strength: Yield (Proof), MPa | 210 | |
| 510 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 300 |
| Maximum Temperature: Corrosion, °C | 560 | |
| 450 |
| Maximum Temperature: Mechanical, °C | 1100 | |
| 1100 |
| Melting Completion (Liquidus), °C | 1410 | |
| 1440 |
| Melting Onset (Solidus), °C | 1360 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Expansion, µm/m-K | 16 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 37 | |
| 17 |
| Density, g/cm3 | 8.0 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 6.2 | |
| 3.4 |
| Embodied Energy, MJ/kg | 89 | |
| 48 |
| Embodied Water, L/kg | 220 | |
| 170 |
Common Calculations
| PREN (Pitting Resistance) | 27 | |
| 36 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 150 | |
| 180 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 110 | |
| 650 |
| Stiffness to Weight: Axial, points | 14 | |
| 15 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 20 | |
| 26 |
| Strength to Weight: Bending, points | 19 | |
| 23 |
| Thermal Shock Resistance, points | 13 | |
| 20 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.025 | |
| 0 |
| Carbon (C), % | 0.040 to 0.080 | |
| 0 to 0.060 |
| Cerium (Ce), % | 0.050 to 0.1 | |
| 0 |
| Chromium (Cr), % | 26 to 28 | |
| 24 to 27 |
| Iron (Fe), % | 36.5 to 42.3 | |
| 62.1 to 70.1 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 1.8 to 2.5 |
| Nickel (Ni), % | 31 to 33 | |
| 4.0 to 6.0 |
| Niobium (Nb), % | 0.6 to 1.0 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0.15 to 0.25 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.3 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.040 |