S33550 Stainless Steel vs. N12160 Nickel

S33550 stainless steel belongs to the iron alloys classification, while N12160 nickel belongs to the nickel alloys. They have 48% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is S33550 stainless steel and the bottom bar is N12160 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
210
Elongation at Break, % 40
45
Fatigue Strength, MPa 270
230
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 79
80
Shear Strength, MPa 470
500
Tensile Strength: Ultimate (UTS), MPa 680
710
Tensile Strength: Yield (Proof), MPa 310
270

Thermal Properties

Latent Heat of Fusion, J/g 300
360
Maximum Temperature: Mechanical, °C 1100
1060
Melting Completion (Liquidus), °C 1400
1330
Melting Onset (Solidus), °C 1360
1280
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
11
Thermal Expansion, µm/m-K 16
13

Otherwise Unclassified Properties

Base Metal Price, % relative 24
90
Density, g/cm3 7.8
8.2
Embodied Carbon, kg CO2/kg material 4.3
8.5
Embodied Energy, MJ/kg 61
120
Embodied Water, L/kg 190
400

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
260
Resilience: Unit (Modulus of Resilience), kJ/m3 250
180
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 24
24
Strength to Weight: Bending, points 22
22
Thermal Diffusivity, mm2/s 3.9
2.8
Thermal Shock Resistance, points 15
19

Alloy Composition

Carbon (C), % 0.040 to 0.1
0 to 0.15
Cerium (Ce), % 0.025 to 0.070
0
Chromium (Cr), % 25 to 28
26 to 30
Cobalt (Co), % 0
27 to 33
Iron (Fe), % 48.8 to 58.2
0 to 3.5
Lanthanum (La), % 0.025 to 0.070
0
Manganese (Mn), % 0 to 1.5
0 to 1.5
Molybdenum (Mo), % 0
0 to 1.0
Nickel (Ni), % 16.5 to 20
25 to 44.4
Niobium (Nb), % 0.050 to 0.15
0 to 1.0
Nitrogen (N), % 0.18 to 0.25
0
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 1.0
2.4 to 3.0
Sulfur (S), % 0 to 0.030
0 to 0.015
Titanium (Ti), % 0
0.2 to 0.8
Tungsten (W), % 0
0 to 1.0