S35000 Stainless Steel vs. ASTM A182 Grade F3V
Both S35000 stainless steel and ASTM A182 grade F3V are iron alloys. They have 79% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is S35000 stainless steel and the bottom bar is ASTM A182 grade F3V.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 2.3 to 14 | |
| 20 |
| Fatigue Strength, MPa | 380 to 520 | |
| 330 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 78 | |
| 74 |
| Shear Strength, MPa | 740 to 950 | |
| 410 |
| Tensile Strength: Ultimate (UTS), MPa | 1300 to 1570 | |
| 660 |
| Tensile Strength: Yield (Proof), MPa | 660 to 1160 | |
| 470 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 900 | |
| 470 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1470 |
| Melting Onset (Solidus), °C | 1410 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 16 | |
| 39 |
| Thermal Expansion, µm/m-K | 11 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.3 | |
| 7.6 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.6 | |
| 8.8 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 14 | |
| 4.2 |
| Density, g/cm3 | 7.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 3.2 | |
| 2.3 |
| Embodied Energy, MJ/kg | 44 | |
| 33 |
| Embodied Water, L/kg | 130 | |
| 63 |
Common Calculations
| PREN (Pitting Resistance) | 28 | |
| 6.3 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 28 to 170 | |
| 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1070 to 3360 | |
| 590 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 46 to 56 | |
| 23 |
| Strength to Weight: Bending, points | 34 to 38 | |
| 21 |
| Thermal Diffusivity, mm2/s | 4.4 | |
| 10 |
| Thermal Shock Resistance, points | 42 to 51 | |
| 19 |
Alloy Composition
| Boron (B), % | 0 | |
| 0.0010 to 0.0030 |
| Carbon (C), % | 0.070 to 0.11 | |
| 0.050 to 0.18 |
| Chromium (Cr), % | 16 to 17 | |
| 2.8 to 3.2 |
| Iron (Fe), % | 72.7 to 76.9 | |
| 94.4 to 95.7 |
| Manganese (Mn), % | 0.5 to 1.3 | |
| 0.3 to 0.6 |
| Molybdenum (Mo), % | 2.5 to 3.2 | |
| 0.9 to 1.1 |
| Nickel (Ni), % | 4.0 to 5.0 | |
| 0 |
| Nitrogen (N), % | 0.070 to 0.13 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.020 |
| Titanium (Ti), % | 0 | |
| 0.015 to 0.035 |
| Vanadium (V), % | 0 | |
| 0.2 to 0.3 |