S35000 Stainless Steel vs. EN 1.4923 Stainless Steel
Both S35000 stainless steel and EN 1.4923 stainless steel are iron alloys. They have 89% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is S35000 stainless steel and the bottom bar is EN 1.4923 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 2.3 to 14 | |
| 12 to 21 |
| Fatigue Strength, MPa | 380 to 520 | |
| 300 to 440 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 78 | |
| 76 |
| Shear Strength, MPa | 740 to 950 | |
| 540 to 590 |
| Tensile Strength: Ultimate (UTS), MPa | 1300 to 1570 | |
| 870 to 980 |
| Tensile Strength: Yield (Proof), MPa | 660 to 1160 | |
| 470 to 780 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 270 |
| Maximum Temperature: Corrosion, °C | 410 | |
| 380 |
| Maximum Temperature: Mechanical, °C | 900 | |
| 740 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1450 |
| Melting Onset (Solidus), °C | 1410 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 16 | |
| 24 |
| Thermal Expansion, µm/m-K | 11 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.3 | |
| 2.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.6 | |
| 3.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 14 | |
| 8.0 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 3.2 | |
| 2.9 |
| Embodied Energy, MJ/kg | 44 | |
| 41 |
| Embodied Water, L/kg | 130 | |
| 100 |
Common Calculations
| PREN (Pitting Resistance) | 28 | |
| 15 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 28 to 170 | |
| 110 to 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1070 to 3360 | |
| 570 to 1580 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 46 to 56 | |
| 31 to 35 |
| Strength to Weight: Bending, points | 34 to 38 | |
| 26 to 28 |
| Thermal Diffusivity, mm2/s | 4.4 | |
| 6.5 |
| Thermal Shock Resistance, points | 42 to 51 | |
| 30 to 34 |
Alloy Composition
| Carbon (C), % | 0.070 to 0.11 | |
| 0.18 to 0.24 |
| Chromium (Cr), % | 16 to 17 | |
| 11 to 12.5 |
| Iron (Fe), % | 72.7 to 76.9 | |
| 83.5 to 87.1 |
| Manganese (Mn), % | 0.5 to 1.3 | |
| 0.4 to 0.9 |
| Molybdenum (Mo), % | 2.5 to 3.2 | |
| 0.8 to 1.2 |
| Nickel (Ni), % | 4.0 to 5.0 | |
| 0.3 to 0.8 |
| Nitrogen (N), % | 0.070 to 0.13 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.015 |
| Vanadium (V), % | 0 | |
| 0.25 to 0.35 |