S35115 Stainless Steel vs. Grade 1 Babbitt Metal

S35115 stainless steel belongs to the iron alloys classification, while grade 1 Babbitt Metal belongs to the otherwise unclassified metals. There are 23 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is S35115 stainless steel and the bottom bar is grade 1 Babbitt Metal.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
13
Elastic (Young's, Tensile) Modulus, GPa 200
53
Elongation at Break, % 46
34
Poisson's Ratio 0.28
0.35
Shear Modulus, GPa 79
20
Tensile Strength: Yield (Proof), MPa 310
30

Thermal Properties

Latent Heat of Fusion, J/g 310
70
Melting Completion (Liquidus), °C 1420
370
Melting Onset (Solidus), °C 1370
220
Specific Heat Capacity, J/kg-K 480
230
Thermal Conductivity, W/m-K 15
45
Thermal Expansion, µm/m-K 16
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
13
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
16

Otherwise Unclassified Properties

Base Metal Price, % relative 26
75
Density, g/cm3 7.9
7.3
Embodied Carbon, kg CO2/kg material 4.8
12
Embodied Energy, MJ/kg 67
200
Embodied Water, L/kg 190
1160

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m3 240
8.6
Stiffness to Weight: Axial, points 14
4.0
Stiffness to Weight: Bending, points 25
17
Thermal Diffusivity, mm2/s 3.9
26

Alloy Composition

Aluminum (Al), % 0
0 to 0.0050
Antimony (Sb), % 0
4.0 to 5.0
Arsenic (As), % 0
0 to 0.1
Bismuth (Bi), % 0
0 to 0.080
Cadmium (Cd), % 0
0 to 0.050
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 23 to 25
0
Copper (Cu), % 0
4.0 to 5.0
Iron (Fe), % 47.6 to 55.8
0 to 0.080
Lead (Pb), % 0
0 to 0.35
Manganese (Mn), % 0 to 1.0
0
Molybdenum (Mo), % 1.5 to 2.5
0
Nickel (Ni), % 19 to 22
0
Nitrogen (N), % 0.2 to 0.3
0
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 0.5 to 1.5
0
Sulfur (S), % 0 to 0.015
0
Tin (Sn), % 0
89.3 to 92
Zinc (Zn), % 0
0 to 0.0050