S35125 Stainless Steel vs. EN 1.1104 Steel

Both S35125 stainless steel and EN 1.1104 steel are iron alloys. They have 43% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is S35125 stainless steel and the bottom bar is EN 1.1104 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 39
27
Fatigue Strength, MPa 200
210
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
73
Shear Strength, MPa 370
280
Tensile Strength: Ultimate (UTS), MPa 540
440
Tensile Strength: Yield (Proof), MPa 230
280

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1430
1460
Melting Onset (Solidus), °C 1380
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 12
49
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 36
2.3
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 6.4
1.5
Embodied Energy, MJ/kg 89
20
Embodied Water, L/kg 210
49

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
100
Resilience: Unit (Modulus of Resilience), kJ/m3 140
200
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 19
15
Strength to Weight: Bending, points 18
16
Thermal Diffusivity, mm2/s 3.1
13
Thermal Shock Resistance, points 12
14

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.024
Carbon (C), % 0 to 0.1
0 to 0.16
Chromium (Cr), % 20 to 23
0 to 0.3
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 36.2 to 45.8
96.6 to 99.38
Manganese (Mn), % 1.0 to 1.5
0.6 to 1.5
Molybdenum (Mo), % 2.0 to 3.0
0 to 0.080
Nickel (Ni), % 31 to 35
0 to 0.5
Niobium (Nb), % 0.25 to 0.6
0 to 0.050
Nitrogen (N), % 0
0 to 0.012
Phosphorus (P), % 0 to 0.045
0 to 0.020
Silicon (Si), % 0 to 0.5
0 to 0.4
Sulfur (S), % 0 to 0.015
0 to 0.0050
Titanium (Ti), % 0
0 to 0.030
Vanadium (V), % 0
0 to 0.050