S35140 Stainless Steel vs. AWS E308Mo

Both S35140 stainless steel and AWS E308Mo are iron alloys. They have 82% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is S35140 stainless steel and the bottom bar is AWS E308Mo.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
40
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 78
78
Tensile Strength: Ultimate (UTS), MPa 690
620

Thermal Properties

Latent Heat of Fusion, J/g 300
290
Melting Completion (Liquidus), °C 1420
1440
Melting Onset (Solidus), °C 1370
1400
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 14
16
Thermal Expansion, µm/m-K 16
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
2.3

Otherwise Unclassified Properties

Base Metal Price, % relative 31
19
Density, g/cm3 8.0
7.9
Embodied Carbon, kg CO2/kg material 5.5
3.8
Embodied Energy, MJ/kg 78
53
Embodied Water, L/kg 190
160

Common Calculations

PREN (Pitting Resistance) 28
28
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 24
22
Strength to Weight: Bending, points 22
20
Thermal Diffusivity, mm2/s 3.7
4.2
Thermal Shock Resistance, points 16
16

Alloy Composition

Carbon (C), % 0 to 0.1
0 to 0.080
Chromium (Cr), % 20 to 22
18 to 21
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 44.1 to 52.7
59.6 to 70.5
Manganese (Mn), % 1.0 to 3.0
0.5 to 2.5
Molybdenum (Mo), % 1.0 to 2.0
2.0 to 3.0
Nickel (Ni), % 25 to 27
9.0 to 12
Niobium (Nb), % 0.25 to 0.75
0
Nitrogen (N), % 0.080 to 0.2
0
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 0.75
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030