S35140 Stainless Steel vs. Solder Alloy 601

S35140 stainless steel belongs to the iron alloys classification, while solder alloy 601 belongs to the otherwise unclassified metals. There are 22 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is S35140 stainless steel and the bottom bar is solder alloy 601.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
5.0
Elastic (Young's, Tensile) Modulus, GPa 200
31
Elongation at Break, % 34
83
Poisson's Ratio 0.28
0.41
Shear Modulus, GPa 78
11
Tensile Strength: Ultimate (UTS), MPa 690
12

Thermal Properties

Latent Heat of Fusion, J/g 300
43
Melting Completion (Liquidus), °C 1420
120
Melting Onset (Solidus), °C 1370
120
Specific Heat Capacity, J/kg-K 470
230
Thermal Conductivity, W/m-K 14
34
Thermal Expansion, µm/m-K 16
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
12
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
14

Otherwise Unclassified Properties

Density, g/cm3 8.0
7.3
Embodied Water, L/kg 190
1330

Common Calculations

Stiffness to Weight: Axial, points 14
2.3
Stiffness to Weight: Bending, points 24
14
Strength to Weight: Axial, points 24
0.45
Strength to Weight: Bending, points 22
1.6
Thermal Diffusivity, mm2/s 3.7
20
Thermal Shock Resistance, points 16
1.2

Alloy Composition

Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.1
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0
0 to 0.0020
Carbon (C), % 0 to 0.1
0
Chromium (Cr), % 20 to 22
0
Copper (Cu), % 0
0 to 0.050
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
51 to 52.5
Iron (Fe), % 44.1 to 52.7
0 to 0.020
Lead (Pb), % 0
0 to 0.070
Manganese (Mn), % 1.0 to 3.0
0
Molybdenum (Mo), % 1.0 to 2.0
0
Nickel (Ni), % 25 to 27
0 to 0.010
Niobium (Nb), % 0.25 to 0.75
0
Nitrogen (N), % 0.080 to 0.2
0
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 0 to 0.75
0
Silver (Ag), % 0
0 to 0.1
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0
47.5 to 48.5
Zinc (Zn), % 0
0 to 0.0010