S35315 Stainless Steel vs. R56406 Titanium

S35315 stainless steel belongs to the iron alloys classification, while R56406 titanium belongs to the titanium alloys. There are 29 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is S35315 stainless steel and the bottom bar is R56406 titanium.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
110
Elongation at Break, % 46
9.1
Fatigue Strength, MPa 280
480
Poisson's Ratio 0.28
0.32
Shear Modulus, GPa 78
40
Tensile Strength: Ultimate (UTS), MPa 740
980
Tensile Strength: Yield (Proof), MPa 300
850

Thermal Properties

Latent Heat of Fusion, J/g 330
410
Maximum Temperature: Mechanical, °C 1100
340
Melting Completion (Liquidus), °C 1370
1610
Melting Onset (Solidus), °C 1330
1560
Specific Heat Capacity, J/kg-K 480
560
Thermal Conductivity, W/m-K 12
7.1
Thermal Expansion, µm/m-K 16
9.6

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
1.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
2.0

Otherwise Unclassified Properties

Base Metal Price, % relative 34
36
Density, g/cm3 7.9
4.5
Embodied Carbon, kg CO2/kg material 5.7
38
Embodied Energy, MJ/kg 81
610
Embodied Water, L/kg 220
200

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 270
85
Resilience: Unit (Modulus of Resilience), kJ/m3 230
3420
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
35
Strength to Weight: Axial, points 26
61
Strength to Weight: Bending, points 23
49
Thermal Diffusivity, mm2/s 3.1
2.8
Thermal Shock Resistance, points 17
69

Alloy Composition

Aluminum (Al), % 0
5.5 to 6.8
Carbon (C), % 0.040 to 0.080
0 to 0.1
Cerium (Ce), % 0.030 to 0.1
0
Chromium (Cr), % 24 to 26
0
Hydrogen (H), % 0
0 to 0.015
Iron (Fe), % 33.6 to 40.6
0 to 0.3
Manganese (Mn), % 0 to 2.0
0
Nickel (Ni), % 34 to 36
0
Nitrogen (N), % 0.12 to 0.18
0 to 0.050
Oxygen (O), % 0
0 to 0.2
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 1.2 to 2.0
0
Sulfur (S), % 0 to 0.030
0
Titanium (Ti), % 0
88.1 to 91
Vanadium (V), % 0
3.5 to 4.5