S35500 Stainless Steel vs. EN 1.1133 Steel

Both S35500 stainless steel and EN 1.1133 steel are iron alloys. They have 77% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is S35500 stainless steel and the bottom bar is EN 1.1133 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 14
19 to 24
Fatigue Strength, MPa 690 to 730
230 to 310
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
73
Shear Strength, MPa 810 to 910
370 to 380
Tensile Strength: Ultimate (UTS), MPa 1330 to 1490
580 to 620
Tensile Strength: Yield (Proof), MPa 1200 to 1280
320 to 460

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 870
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 16
49
Thermal Expansion, µm/m-K 11
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 16
2.1
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.5
1.5
Embodied Energy, MJ/kg 47
19
Embodied Water, L/kg 130
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180 to 190
110 to 120
Resilience: Unit (Modulus of Resilience), kJ/m3 3610 to 4100
270 to 550
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 47 to 53
21 to 22
Strength to Weight: Bending, points 34 to 37
20 to 21
Thermal Diffusivity, mm2/s 4.4
13
Thermal Shock Resistance, points 44 to 49
18 to 19

Alloy Composition

Carbon (C), % 0.1 to 0.15
0.17 to 0.23
Chromium (Cr), % 15 to 16
0 to 0.4
Iron (Fe), % 73.2 to 77.7
96.9 to 98.8
Manganese (Mn), % 0.5 to 1.3
1.0 to 1.5
Molybdenum (Mo), % 2.5 to 3.2
0 to 0.1
Nickel (Ni), % 4.0 to 5.0
0 to 0.4
Niobium (Nb), % 0.1 to 0.5
0
Nitrogen (N), % 0.070 to 0.13
0
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 0.5
0 to 0.4
Sulfur (S), % 0 to 0.030
0 to 0.035

Comparable Variants