S35500 Stainless Steel vs. SAE-AISI 50B46 Steel
Both S35500 stainless steel and SAE-AISI 50B46 steel are iron alloys. They have 77% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is S35500 stainless steel and the bottom bar is SAE-AISI 50B46 steel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 200 | |
190 |
Elongation at Break, % | 14 | |
21 |
Fatigue Strength, MPa | 690 to 730 | |
220 |
Poisson's Ratio | 0.28 | |
0.29 |
Shear Modulus, GPa | 78 | |
72 |
Shear Strength, MPa | 810 to 910 | |
340 |
Tensile Strength: Ultimate (UTS), MPa | 1330 to 1490 | |
540 |
Tensile Strength: Yield (Proof), MPa | 1200 to 1280 | |
310 |
Thermal Properties
Latent Heat of Fusion, J/g | 280 | |
250 |
Maximum Temperature: Mechanical, °C | 870 | |
410 |
Melting Completion (Liquidus), °C | 1460 | |
1460 |
Melting Onset (Solidus), °C | 1420 | |
1420 |
Specific Heat Capacity, J/kg-K | 470 | |
470 |
Thermal Conductivity, W/m-K | 16 | |
47 |
Thermal Expansion, µm/m-K | 11 | |
13 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
7.1 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 2.5 | |
8.2 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 16 | |
1.9 |
Density, g/cm3 | 7.8 | |
7.8 |
Embodied Carbon, kg CO2/kg material | 3.5 | |
1.4 |
Embodied Energy, MJ/kg | 47 | |
19 |
Embodied Water, L/kg | 130 | |
47 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 to 190 | |
99 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 3610 to 4100 | |
260 |
Stiffness to Weight: Axial, points | 14 | |
13 |
Stiffness to Weight: Bending, points | 25 | |
24 |
Strength to Weight: Axial, points | 47 to 53 | |
19 |
Strength to Weight: Bending, points | 34 to 37 | |
19 |
Thermal Diffusivity, mm2/s | 4.4 | |
13 |
Thermal Shock Resistance, points | 44 to 49 | |
16 |
Alloy Composition
Boron (B), % | 0 | |
0.00050 to 0.0030 |
Carbon (C), % | 0.1 to 0.15 | |
0.44 to 0.49 |
Chromium (Cr), % | 15 to 16 | |
0.2 to 0.35 |
Iron (Fe), % | 73.2 to 77.7 | |
97.7 to 98.5 |
Manganese (Mn), % | 0.5 to 1.3 | |
0.75 to 1.0 |
Molybdenum (Mo), % | 2.5 to 3.2 | |
0 |
Nickel (Ni), % | 4.0 to 5.0 | |
0 |
Niobium (Nb), % | 0.1 to 0.5 | |
0 |
Nitrogen (N), % | 0.070 to 0.13 | |
0 |
Phosphorus (P), % | 0 to 0.040 | |
0 to 0.035 |
Silicon (Si), % | 0 to 0.5 | |
0.15 to 0.35 |
Sulfur (S), % | 0 to 0.030 | |
0 to 0.040 |