S35500 Stainless Steel vs. K94200 Alloy
Both S35500 stainless steel and K94200 alloy are iron alloys. There are 22 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is S35500 stainless steel and the bottom bar is K94200 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 200 | |
140 |
Elongation at Break, % | 14 | |
5.0 to 32 |
Poisson's Ratio | 0.28 | |
0.34 |
Shear Modulus, GPa | 78 | |
54 |
Shear Strength, MPa | 810 to 910 | |
330 to 410 |
Tensile Strength: Ultimate (UTS), MPa | 1330 to 1490 | |
500 to 710 |
Tensile Strength: Yield (Proof), MPa | 1200 to 1280 | |
270 to 650 |
Thermal Properties
Melting Onset (Solidus), °C | 1420 | |
1440 |
Specific Heat Capacity, J/kg-K | 470 | |
500 |
Thermal Conductivity, W/m-K | 16 | |
15 |
Thermal Expansion, µm/m-K | 11 | |
5.0 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
2.7 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 2.5 | |
3.0 |
Otherwise Unclassified Properties
Density, g/cm3 | 7.8 | |
8.2 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 to 190 | |
35 to 130 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 3610 to 4100 | |
250 to 1460 |
Stiffness to Weight: Axial, points | 14 | |
9.8 |
Stiffness to Weight: Bending, points | 25 | |
21 |
Strength to Weight: Axial, points | 47 to 53 | |
17 to 24 |
Strength to Weight: Bending, points | 34 to 37 | |
17 to 22 |
Thermal Diffusivity, mm2/s | 4.4 | |
3.7 |
Thermal Shock Resistance, points | 44 to 49 | |
49 to 70 |