S35500 Stainless Steel vs. Z41321 Zinc
S35500 stainless steel belongs to the iron alloys classification, while Z41321 zinc belongs to the zinc alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is S35500 stainless steel and the bottom bar is Z41321 zinc.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 87 |
| Elongation at Break, % | 14 | |
| 60 |
| Poisson's Ratio | 0.28 | |
| 0.25 |
| Shear Modulus, GPa | 78 | |
| 35 |
| Tensile Strength: Ultimate (UTS), MPa | 1330 to 1490 | |
| 190 |
| Tensile Strength: Yield (Proof), MPa | 1200 to 1280 | |
| 150 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 110 |
| Maximum Temperature: Mechanical, °C | 870 | |
| 90 |
| Melting Completion (Liquidus), °C | 1460 | |
| 410 |
| Melting Onset (Solidus), °C | 1420 | |
| 400 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 390 |
| Thermal Conductivity, W/m-K | 16 | |
| 110 |
| Thermal Expansion, µm/m-K | 11 | |
| 26 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
| 27 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.5 | |
| 37 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 16 | |
| 12 |
| Density, g/cm3 | 7.8 | |
| 6.6 |
| Embodied Carbon, kg CO2/kg material | 3.5 | |
| 2.8 |
| Embodied Energy, MJ/kg | 47 | |
| 54 |
| Embodied Water, L/kg | 130 | |
| 340 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 to 190 | |
| 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 3610 to 4100 | |
| 130 |
| Stiffness to Weight: Axial, points | 14 | |
| 7.4 |
| Stiffness to Weight: Bending, points | 25 | |
| 23 |
| Strength to Weight: Axial, points | 47 to 53 | |
| 7.9 |
| Strength to Weight: Bending, points | 34 to 37 | |
| 11 |
| Thermal Diffusivity, mm2/s | 4.4 | |
| 44 |
| Thermal Shock Resistance, points | 44 to 49 | |
| 5.9 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.010 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0050 |
| Carbon (C), % | 0.1 to 0.15 | |
| 0 |
| Chromium (Cr), % | 15 to 16 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0.5 to 1.0 |
| Iron (Fe), % | 73.2 to 77.7 | |
| 0 to 0.010 |
| Lead (Pb), % | 0 | |
| 0 to 0.010 |
| Manganese (Mn), % | 0.5 to 1.3 | |
| 0 |
| Molybdenum (Mo), % | 2.5 to 3.2 | |
| 0 |
| Nickel (Ni), % | 4.0 to 5.0 | |
| 0 |
| Niobium (Nb), % | 0.1 to 0.5 | |
| 0 |
| Nitrogen (N), % | 0.070 to 0.13 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 0.0030 |
| Titanium (Ti), % | 0 | |
| 0.080 to 0.18 |
| Zinc (Zn), % | 0 | |
| 98.8 to 99.42 |