S36200 Stainless Steel vs. EN 1.4876 Stainless Steel

Both S36200 stainless steel and EN 1.4876 stainless steel are iron alloys. They have 67% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is S36200 stainless steel and the bottom bar is EN 1.4876 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 3.4 to 4.6
33
Fatigue Strength, MPa 450 to 570
150
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
77
Shear Strength, MPa 680 to 810
370
Tensile Strength: Ultimate (UTS), MPa 1180 to 1410
570
Tensile Strength: Yield (Proof), MPa 960 to 1240
190

Thermal Properties

Latent Heat of Fusion, J/g 280
300
Maximum Temperature: Corrosion, °C 530
490
Maximum Temperature: Mechanical, °C 820
1100
Melting Completion (Liquidus), °C 1440
1400
Melting Onset (Solidus), °C 1400
1350
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 16
12
Thermal Expansion, µm/m-K 11
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 12
30
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 2.8
5.3
Embodied Energy, MJ/kg 40
76
Embodied Water, L/kg 120
200

Common Calculations

PREN (Pitting Resistance) 15
21
Resilience: Ultimate (Unit Rupture Work), MJ/m3 46 to 51
140
Resilience: Unit (Modulus of Resilience), kJ/m3 2380 to 3930
94
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 42 to 50
20
Strength to Weight: Bending, points 32 to 36
19
Thermal Diffusivity, mm2/s 4.3
3.2
Thermal Shock Resistance, points 40 to 48
14

Alloy Composition

Aluminum (Al), % 0 to 0.1
0.15 to 0.6
Carbon (C), % 0 to 0.050
0 to 0.12
Chromium (Cr), % 14 to 14.5
19 to 23
Iron (Fe), % 75.4 to 79.5
38.6 to 50.7
Manganese (Mn), % 0 to 0.5
0 to 2.0
Molybdenum (Mo), % 0 to 0.3
0
Nickel (Ni), % 6.5 to 7.0
30 to 34
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0 to 0.3
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015
Titanium (Ti), % 0.6 to 0.9
0.15 to 0.6