S38100 Stainless Steel vs. EN 1.3975 Stainless Steel

Both S38100 stainless steel and EN 1.3975 stainless steel are iron alloys. They have 90% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is S38100 stainless steel and the bottom bar is EN 1.3975 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
190
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 45
27
Fatigue Strength, MPa 210
230
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
76
Tensile Strength: Ultimate (UTS), MPa 580
660
Tensile Strength: Yield (Proof), MPa 230
320

Thermal Properties

Latent Heat of Fusion, J/g 320
340
Maximum Temperature: Corrosion, °C 410
410
Maximum Temperature: Mechanical, °C 970
910
Melting Completion (Liquidus), °C 1400
1360
Melting Onset (Solidus), °C 1350
1320
Specific Heat Capacity, J/kg-K 480
500
Thermal Expansion, µm/m-K 16
16

Otherwise Unclassified Properties

Base Metal Price, % relative 20
15
Density, g/cm3 7.8
7.5
Embodied Carbon, kg CO2/kg material 3.8
3.3
Embodied Energy, MJ/kg 54
47
Embodied Water, L/kg 160
150

Common Calculations

PREN (Pitting Resistance) 18
21
Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
150
Resilience: Unit (Modulus of Resilience), kJ/m3 140
270
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
26
Strength to Weight: Axial, points 21
24
Strength to Weight: Bending, points 20
22
Thermal Shock Resistance, points 13
15

Alloy Composition

Carbon (C), % 0 to 0.080
0 to 0.050
Chromium (Cr), % 17 to 19
16 to 18
Iron (Fe), % 57.9 to 64
58.2 to 65.4
Manganese (Mn), % 0 to 2.0
7.0 to 9.0
Molybdenum (Mo), % 0
0 to 1.0
Nickel (Ni), % 17.5 to 18.5
8.0 to 9.0
Nitrogen (N), % 0
0.080 to 0.18
Phosphorus (P), % 0 to 0.030
0 to 0.045
Silicon (Si), % 1.5 to 2.5
3.5 to 4.5
Sulfur (S), % 0 to 0.030
0 to 0.030