S38100 Stainless Steel vs. EN 1.6523 Steel

Both S38100 stainless steel and EN 1.6523 steel are iron alloys. They have 63% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is S38100 stainless steel and the bottom bar is EN 1.6523 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
150 to 190
Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Tensile Strength: Ultimate (UTS), MPa 580
510 to 1460

Thermal Properties

Latent Heat of Fusion, J/g 320
250
Maximum Temperature: Mechanical, °C 970
410
Melting Completion (Liquidus), °C 1400
1460
Melting Onset (Solidus), °C 1350
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
39
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 20
2.6
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 3.8
1.5
Embodied Energy, MJ/kg 54
20
Embodied Water, L/kg 160
50

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
18 to 52
Strength to Weight: Bending, points 20
18 to 36
Thermal Diffusivity, mm2/s 4.0
10
Thermal Shock Resistance, points 13
15 to 43

Alloy Composition

Carbon (C), % 0 to 0.080
0.17 to 0.23
Chromium (Cr), % 17 to 19
0.35 to 0.7
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 57.9 to 64
96.6 to 98.3
Manganese (Mn), % 0 to 2.0
0.65 to 1.0
Molybdenum (Mo), % 0
0.15 to 0.25
Nickel (Ni), % 17.5 to 18.5
0.4 to 0.7
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 1.5 to 2.5
0 to 0.3
Sulfur (S), % 0 to 0.030
0 to 0.025