S38815 Stainless Steel vs. AWS ERNiCu-7

S38815 stainless steel belongs to the iron alloys classification, while AWS ERNiCu-7 belongs to the nickel alloys. There are 20 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is S38815 stainless steel and the bottom bar is AWS ERNiCu-7.

UNS S38815 Stainless Steel AWS ERNiCu-7 (N04060) Weld Metal

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		190
Elastic (Young's, Tensile) Modulus, GPa		160

Elongation at Break, %		34
Elongation at Break, %		34

Poisson's Ratio		0.29
Poisson's Ratio		0.32

Shear Modulus, GPa		74
Shear Modulus, GPa		61

Tensile Strength: Ultimate (UTS), MPa		610
Tensile Strength: Ultimate (UTS), MPa		550

Thermal Properties

Latent Heat of Fusion, J/g		370
Latent Heat of Fusion, J/g		280

Melting Completion (Liquidus), °C		1360
Melting Completion (Liquidus), °C		1280

Melting Onset (Solidus), °C		1310
Melting Onset (Solidus), °C		1240

Specific Heat Capacity, J/kg-K		500
Specific Heat Capacity, J/kg-K		440

Thermal Expansion, µm/m-K		15
Thermal Expansion, µm/m-K		13

Otherwise Unclassified Properties

Base Metal Price, % relative		19
Base Metal Price, % relative		50

Density, g/cm³		7.5
Density, g/cm³		8.7

Embodied Carbon, kg CO₂/kg material		3.8
Embodied Carbon, kg CO₂/kg material		8.5

Embodied Energy, MJ/kg		54
Embodied Energy, MJ/kg		120

Embodied Water, L/kg		140
Embodied Water, L/kg		250

Common Calculations

Stiffness to Weight: Axial, points		14
Stiffness to Weight: Axial, points		10

Stiffness to Weight: Bending, points		25
Stiffness to Weight: Bending, points		21

Strength to Weight: Axial, points		22
Strength to Weight: Axial, points		18

Strength to Weight: Bending, points		21
Strength to Weight: Bending, points		17

Thermal Shock Resistance, points		15
Thermal Shock Resistance, points		19

Alloy Composition

Aluminum (Al), %		0 to 0.3
Aluminum (Al), %		0 to 1.3

Carbon (C), %		0 to 0.030
Carbon (C), %		0 to 0.15

Chromium (Cr), %		13 to 15
Chromium (Cr), %		0

Copper (Cu), %		0.75 to 1.5
Copper (Cu), %		18.3 to 36.5

Iron (Fe), %		56.1 to 67
Iron (Fe), %		0 to 2.5

Manganese (Mn), %		0 to 2.0
Manganese (Mn), %		0 to 4.0

Molybdenum (Mo), %		0.75 to 1.5
Molybdenum (Mo), %		0

Nickel (Ni), %		13 to 17
Nickel (Ni), %		62 to 69

Phosphorus (P), %		0 to 0.040
Phosphorus (P), %		0 to 0.030

Silicon (Si), %		5.5 to 6.5
Silicon (Si), %		0 to 1.3

Sulfur (S), %		0 to 0.020
Sulfur (S), %		0 to 0.015

Titanium (Ti), %		0
Titanium (Ti), %		1.5 to 3.0

Residuals, %		0
Residuals, %		0 to 0.5