S40920 Stainless Steel vs. AISI 304L Stainless Steel
Both S40920 stainless steel and AISI 304L stainless steel are iron alloys. They have 82% of their average alloy composition in common. There are 34 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is S40920 stainless steel and the bottom bar is AISI 304L stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
Brinell Hardness | 150 | |
160 to 350 |
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
200 |
Elongation at Break, % | 22 | |
6.7 to 46 |
Fatigue Strength, MPa | 130 | |
170 to 430 |
Poisson's Ratio | 0.28 | |
0.28 |
Rockwell B Hardness | 77 | |
79 |
Shear Modulus, GPa | 75 | |
77 |
Shear Strength, MPa | 270 | |
370 to 680 |
Tensile Strength: Ultimate (UTS), MPa | 430 | |
540 to 1160 |
Tensile Strength: Yield (Proof), MPa | 190 | |
190 to 870 |
Thermal Properties
Latent Heat of Fusion, J/g | 270 | |
290 |
Maximum Temperature: Corrosion, °C | 450 | |
420 |
Maximum Temperature: Mechanical, °C | 710 | |
540 |
Melting Completion (Liquidus), °C | 1450 | |
1450 |
Melting Onset (Solidus), °C | 1400 | |
1400 |
Specific Heat Capacity, J/kg-K | 480 | |
480 |
Thermal Conductivity, W/m-K | 26 | |
16 |
Thermal Expansion, µm/m-K | 10 | |
17 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 2.9 | |
2.4 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 3.3 | |
2.7 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 6.5 | |
16 |
Density, g/cm3 | 7.7 | |
7.8 |
Embodied Carbon, kg CO2/kg material | 2.0 | |
3.1 |
Embodied Energy, MJ/kg | 28 | |
44 |
Embodied Water, L/kg | 94 | |
150 |
Common Calculations
PREN (Pitting Resistance) | 11 | |
20 |
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 78 | |
71 to 240 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 97 | |
92 to 1900 |
Stiffness to Weight: Axial, points | 14 | |
14 |
Stiffness to Weight: Bending, points | 25 | |
25 |
Strength to Weight: Axial, points | 15 | |
19 to 41 |
Strength to Weight: Bending, points | 16 | |
19 to 31 |
Thermal Diffusivity, mm2/s | 6.9 | |
4.2 |
Thermal Shock Resistance, points | 15 | |
12 to 25 |
Alloy Composition
Carbon (C), % | 0 to 0.030 | |
0 to 0.030 |
Chromium (Cr), % | 10.5 to 11.7 | |
18 to 20 |
Iron (Fe), % | 85.1 to 89.4 | |
65 to 74 |
Manganese (Mn), % | 0 to 1.0 | |
0 to 2.0 |
Nickel (Ni), % | 0 to 0.5 | |
8.0 to 12 |
Niobium (Nb), % | 0 to 0.1 | |
0 |
Nitrogen (N), % | 0 to 0.030 | |
0 to 0.1 |
Phosphorus (P), % | 0 to 0.040 | |
0 to 0.045 |
Silicon (Si), % | 0 to 1.0 | |
0 to 0.75 |
Sulfur (S), % | 0 to 0.020 | |
0 to 0.030 |
Titanium (Ti), % | 0.15 to 0.5 | |
0 |