S40920 Stainless Steel vs. SAE-AISI 4620 Steel

Both S40920 stainless steel and SAE-AISI 4620 steel are iron alloys. They have 88% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is S40920 stainless steel and the bottom bar is SAE-AISI 4620 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
150 to 210
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 22
16 to 27
Fatigue Strength, MPa 130
260 to 360
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 75
73
Shear Strength, MPa 270
320 to 420
Tensile Strength: Ultimate (UTS), MPa 430
490 to 680
Tensile Strength: Yield (Proof), MPa 190
350 to 550

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Maximum Temperature: Mechanical, °C 710
410
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 26
47
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 6.5
3.2
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 2.0
1.6
Embodied Energy, MJ/kg 28
22
Embodied Water, L/kg 94
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 78
100 to 120
Resilience: Unit (Modulus of Resilience), kJ/m3 97
330 to 800
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 15
17 to 24
Strength to Weight: Bending, points 16
18 to 22
Thermal Diffusivity, mm2/s 6.9
13
Thermal Shock Resistance, points 15
15 to 20

Alloy Composition

Carbon (C), % 0 to 0.030
0.17 to 0.22
Chromium (Cr), % 10.5 to 11.7
0
Iron (Fe), % 85.1 to 89.4
96.4 to 97.4
Manganese (Mn), % 0 to 1.0
0.45 to 0.65
Molybdenum (Mo), % 0
0.2 to 0.3
Nickel (Ni), % 0 to 0.5
1.7 to 2.0
Niobium (Nb), % 0 to 0.1
0
Nitrogen (N), % 0 to 0.030
0
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 1.0
0.15 to 0.35
Sulfur (S), % 0 to 0.020
0 to 0.040
Titanium (Ti), % 0.15 to 0.5
0