S40920 Stainless Steel vs. Z41321 Zinc

S40920 stainless steel belongs to the iron alloys classification, while Z41321 zinc belongs to the zinc alloys. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is S40920 stainless steel and the bottom bar is Z41321 zinc.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
87
Elongation at Break, % 22
60
Poisson's Ratio 0.28
0.25
Shear Modulus, GPa 75
35
Tensile Strength: Ultimate (UTS), MPa 430
190
Tensile Strength: Yield (Proof), MPa 190
150

Thermal Properties

Latent Heat of Fusion, J/g 270
110
Maximum Temperature: Mechanical, °C 710
90
Melting Completion (Liquidus), °C 1450
410
Melting Onset (Solidus), °C 1400
400
Specific Heat Capacity, J/kg-K 480
390
Thermal Conductivity, W/m-K 26
110
Thermal Expansion, µm/m-K 10
26

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
27
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
37

Otherwise Unclassified Properties

Base Metal Price, % relative 6.5
12
Density, g/cm3 7.7
6.6
Embodied Carbon, kg CO2/kg material 2.0
2.8
Embodied Energy, MJ/kg 28
54
Embodied Water, L/kg 94
340

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 78
100
Resilience: Unit (Modulus of Resilience), kJ/m3 97
130
Stiffness to Weight: Axial, points 14
7.4
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 15
7.9
Strength to Weight: Bending, points 16
11
Thermal Diffusivity, mm2/s 6.9
44
Thermal Shock Resistance, points 15
5.9

Alloy Composition

Aluminum (Al), % 0
0 to 0.010
Cadmium (Cd), % 0
0 to 0.0050
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 10.5 to 11.7
0
Copper (Cu), % 0
0.5 to 1.0
Iron (Fe), % 85.1 to 89.4
0 to 0.010
Lead (Pb), % 0
0 to 0.010
Manganese (Mn), % 0 to 1.0
0
Nickel (Ni), % 0 to 0.5
0
Niobium (Nb), % 0 to 0.1
0
Nitrogen (N), % 0 to 0.030
0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.020
0
Tin (Sn), % 0
0 to 0.0030
Titanium (Ti), % 0.15 to 0.5
0.080 to 0.18
Zinc (Zn), % 0
98.8 to 99.42