S41003 Stainless Steel vs. EN 1.3543 Stainless Steel

Both S41003 stainless steel and EN 1.3543 stainless steel are iron alloys. They have a moderately high 94% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is S41003 stainless steel and the bottom bar is EN 1.3543 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200
220
Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
76
Tensile Strength: Ultimate (UTS), MPa 520
730

Thermal Properties

Latent Heat of Fusion, J/g 270
280
Maximum Temperature: Corrosion, °C 390
390
Maximum Temperature: Mechanical, °C 720
870
Melting Completion (Liquidus), °C 1440
1430
Melting Onset (Solidus), °C 1400
1390
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 27
22
Thermal Expansion, µm/m-K 10
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
2.5
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
3.0

Otherwise Unclassified Properties

Base Metal Price, % relative 7.0
9.0
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.9
2.3
Embodied Energy, MJ/kg 27
32
Embodied Water, L/kg 97
120

Common Calculations

PREN (Pitting Resistance) 12
19
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 19
27
Strength to Weight: Bending, points 18
24
Thermal Diffusivity, mm2/s 7.2
6.1
Thermal Shock Resistance, points 19
26

Alloy Composition

Carbon (C), % 0 to 0.030
1.0 to 1.2
Chromium (Cr), % 10.5 to 12.5
16 to 18
Iron (Fe), % 83.4 to 89.5
79.1 to 83.6
Manganese (Mn), % 0 to 1.5
0 to 1.0
Molybdenum (Mo), % 0
0.4 to 0.8
Nickel (Ni), % 0 to 1.5
0
Nitrogen (N), % 0 to 0.030
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030