S41003 Stainless Steel vs. C42200 Brass
S41003 stainless steel belongs to the iron alloys classification, while C42200 brass belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is S41003 stainless steel and the bottom bar is C42200 brass.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
110 |
Elongation at Break, % | 21 | |
2.0 to 46 |
Poisson's Ratio | 0.28 | |
0.33 |
Shear Modulus, GPa | 76 | |
42 |
Shear Strength, MPa | 320 | |
210 to 350 |
Tensile Strength: Ultimate (UTS), MPa | 520 | |
300 to 610 |
Tensile Strength: Yield (Proof), MPa | 310 | |
100 to 570 |
Thermal Properties
Latent Heat of Fusion, J/g | 270 | |
200 |
Maximum Temperature: Mechanical, °C | 720 | |
170 |
Melting Completion (Liquidus), °C | 1440 | |
1040 |
Melting Onset (Solidus), °C | 1400 | |
1020 |
Specific Heat Capacity, J/kg-K | 480 | |
380 |
Thermal Conductivity, W/m-K | 27 | |
130 |
Thermal Expansion, µm/m-K | 10 | |
18 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 2.9 | |
31 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 3.3 | |
32 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 7.0 | |
29 |
Density, g/cm3 | 7.8 | |
8.6 |
Embodied Carbon, kg CO2/kg material | 1.9 | |
2.7 |
Embodied Energy, MJ/kg | 27 | |
44 |
Embodied Water, L/kg | 97 | |
320 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 92 | |
12 to 110 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 240 | |
49 to 1460 |
Stiffness to Weight: Axial, points | 14 | |
7.2 |
Stiffness to Weight: Bending, points | 25 | |
19 |
Strength to Weight: Axial, points | 19 | |
9.5 to 19 |
Strength to Weight: Bending, points | 18 | |
11 to 18 |
Thermal Diffusivity, mm2/s | 7.2 | |
39 |
Thermal Shock Resistance, points | 19 | |
10 to 21 |
Alloy Composition
Carbon (C), % | 0 to 0.030 | |
0 |
Chromium (Cr), % | 10.5 to 12.5 | |
0 |
Copper (Cu), % | 0 | |
86 to 89 |
Iron (Fe), % | 83.4 to 89.5 | |
0 to 0.050 |
Lead (Pb), % | 0 | |
0 to 0.050 |
Manganese (Mn), % | 0 to 1.5 | |
0 |
Nickel (Ni), % | 0 to 1.5 | |
0 |
Nitrogen (N), % | 0 to 0.030 | |
0 |
Phosphorus (P), % | 0 to 0.040 | |
0 to 0.35 |
Silicon (Si), % | 0 to 1.0 | |
0 |
Sulfur (S), % | 0 to 0.030 | |
0 |
Tin (Sn), % | 0 | |
0.8 to 1.4 |
Zinc (Zn), % | 0 | |
8.7 to 13.2 |
Residuals, % | 0 | |
0 to 0.5 |