S41041 Stainless Steel vs. Grade TDSiCrV Steel

Both S41041 stainless steel and grade TDSiCrV steel are iron alloys. They have 88% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is S41041 stainless steel and the bottom bar is grade TDSiCrV steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 240
630
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.28
0.29
Reduction in Area, % 56
48
Shear Modulus, GPa 76
80
Tensile Strength: Ultimate (UTS), MPa 910
2100

Thermal Properties

Latent Heat of Fusion, J/g 270
270
Maximum Temperature: Mechanical, °C 740
420
Melting Completion (Liquidus), °C 1450
1440
Melting Onset (Solidus), °C 1410
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 29
47
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 8.5
2.3
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 2.2
1.9
Embodied Energy, MJ/kg 31
26
Embodied Water, L/kg 100
50

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 32
75
Strength to Weight: Bending, points 27
47
Thermal Diffusivity, mm2/s 7.8
13
Thermal Shock Resistance, points 33
63

Alloy Composition

Aluminum (Al), % 0 to 0.050
0
Carbon (C), % 0.13 to 0.18
0.5 to 0.7
Chromium (Cr), % 11.5 to 13
0.5 to 1.0
Copper (Cu), % 0
0 to 0.1
Iron (Fe), % 84.5 to 87.8
96.1 to 97.8
Manganese (Mn), % 0.4 to 0.6
0.4 to 0.9
Molybdenum (Mo), % 0 to 0.2
0
Nickel (Ni), % 0 to 0.5
0
Niobium (Nb), % 0.15 to 0.45
0
Phosphorus (P), % 0 to 0.030
0 to 0.020
Silicon (Si), % 0 to 0.5
1.2 to 1.7
Sulfur (S), % 0 to 0.030
0 to 0.020
Vanadium (V), % 0
0.1 to 0.25