S41041 Stainless Steel vs. N08926 Stainless Steel

Both S41041 stainless steel and N08926 stainless steel are iron alloys. They have 59% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is S41041 stainless steel and the bottom bar is N08926 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 17
40
Fatigue Strength, MPa 350
290
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
80
Shear Strength, MPa 560
500
Tensile Strength: Ultimate (UTS), MPa 910
740
Tensile Strength: Yield (Proof), MPa 580
330

Thermal Properties

Latent Heat of Fusion, J/g 270
300
Maximum Temperature: Corrosion, °C 430
420
Maximum Temperature: Mechanical, °C 740
1100
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1410
1410
Specific Heat Capacity, J/kg-K 480
460
Thermal Conductivity, W/m-K 29
12
Thermal Expansion, µm/m-K 10
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 8.5
33
Density, g/cm3 7.8
8.1
Embodied Carbon, kg CO2/kg material 2.2
6.2
Embodied Energy, MJ/kg 31
84
Embodied Water, L/kg 100
200

Common Calculations

PREN (Pitting Resistance) 13
45
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
240
Resilience: Unit (Modulus of Resilience), kJ/m3 860
270
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 32
25
Strength to Weight: Bending, points 27
22
Thermal Diffusivity, mm2/s 7.8
3.2
Thermal Shock Resistance, points 33
16

Alloy Composition

Aluminum (Al), % 0 to 0.050
0
Carbon (C), % 0.13 to 0.18
0 to 0.020
Chromium (Cr), % 11.5 to 13
19 to 21
Copper (Cu), % 0
0.5 to 1.5
Iron (Fe), % 84.5 to 87.8
41.7 to 50.4
Manganese (Mn), % 0.4 to 0.6
0 to 2.0
Molybdenum (Mo), % 0 to 0.2
6.0 to 7.0
Nickel (Ni), % 0 to 0.5
24 to 26
Niobium (Nb), % 0.15 to 0.45
0
Nitrogen (N), % 0
0.15 to 0.25
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0 to 0.5
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.010