S42010 Stainless Steel vs. EN 1.4539 Stainless Steel

Both S42010 stainless steel and EN 1.4539 stainless steel are iron alloys. They have 64% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is S42010 stainless steel and the bottom bar is EN 1.4539 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 18
38
Fatigue Strength, MPa 220
220
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
79
Shear Strength, MPa 370
430
Tensile Strength: Ultimate (UTS), MPa 590
630
Tensile Strength: Yield (Proof), MPa 350
260

Thermal Properties

Latent Heat of Fusion, J/g 280
300
Maximum Temperature: Corrosion, °C 390
420
Maximum Temperature: Mechanical, °C 800
1100
Melting Completion (Liquidus), °C 1440
1440
Melting Onset (Solidus), °C 1400
1390
Specific Heat Capacity, J/kg-K 480
460
Thermal Conductivity, W/m-K 29
12
Thermal Expansion, µm/m-K 10
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.7
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 3.2
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 8.5
31
Density, g/cm3 7.7
8.1
Embodied Carbon, kg CO2/kg material 2.2
5.7
Embodied Energy, MJ/kg 30
78
Embodied Water, L/kg 110
200

Common Calculations

PREN (Pitting Resistance) 16
36
Resilience: Ultimate (Unit Rupture Work), MJ/m3 95
190
Resilience: Unit (Modulus of Resilience), kJ/m3 310
160
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
22
Strength to Weight: Bending, points 20
20
Thermal Diffusivity, mm2/s 7.9
3.2
Thermal Shock Resistance, points 21
14

Alloy Composition

Carbon (C), % 0.15 to 0.3
0 to 0.020
Chromium (Cr), % 13.5 to 15
19 to 21
Copper (Cu), % 0
1.2 to 2.0
Iron (Fe), % 80.9 to 85.6
43.1 to 51.8
Manganese (Mn), % 0 to 1.0
0 to 2.0
Molybdenum (Mo), % 0.4 to 0.85
4.0 to 5.0
Nickel (Ni), % 0.35 to 0.85
24 to 26
Nitrogen (N), % 0
0 to 0.15
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 0.7
Sulfur (S), % 0 to 0.030
0 to 0.010