S42035 Stainless Steel vs. AWS E80C-W2

Both S42035 stainless steel and AWS E80C-W2 are iron alloys. They have 84% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is S42035 stainless steel and the bottom bar is AWS E80C-W2.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 18
25
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
72
Tensile Strength: Ultimate (UTS), MPa 630
620
Tensile Strength: Yield (Proof), MPa 430
540

Thermal Properties

Latent Heat of Fusion, J/g 280
260
Melting Completion (Liquidus), °C 1450
1450
Melting Onset (Solidus), °C 1400
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 27
39
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.7
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 3.2
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
2.6
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.4
1.5
Embodied Energy, MJ/kg 34
20
Embodied Water, L/kg 110
51

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
150
Resilience: Unit (Modulus of Resilience), kJ/m3 460
770
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 22
22
Strength to Weight: Bending, points 21
21
Thermal Diffusivity, mm2/s 7.2
10
Thermal Shock Resistance, points 22
18

Alloy Composition

Carbon (C), % 0 to 0.080
0 to 0.12
Chromium (Cr), % 13.5 to 15.5
0.45 to 0.7
Copper (Cu), % 0
0.3 to 0.75
Iron (Fe), % 78.1 to 85
94.9 to 98
Manganese (Mn), % 0 to 1.0
0.5 to 1.3
Molybdenum (Mo), % 0.2 to 1.2
0
Nickel (Ni), % 1.0 to 2.5
0.4 to 0.8
Phosphorus (P), % 0 to 0.045
0 to 0.025
Silicon (Si), % 0 to 1.0
0.35 to 0.8
Sulfur (S), % 0 to 0.030
0 to 0.030
Titanium (Ti), % 0.3 to 0.5
0
Vanadium (V), % 0
0 to 0.030
Residuals, % 0
0 to 0.5