S43037 Stainless Steel vs. ACI-ASTM CG3M Steel

Both S43037 stainless steel and ACI-ASTM CG3M steel are iron alloys. They have 83% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is S43037 stainless steel and the bottom bar is ACI-ASTM CG3M steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
170
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 25
28
Fatigue Strength, MPa 160
200
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
79
Tensile Strength: Ultimate (UTS), MPa 410
580
Tensile Strength: Yield (Proof), MPa 230
270

Thermal Properties

Latent Heat of Fusion, J/g 280
300
Maximum Temperature: Corrosion, °C 510
420
Maximum Temperature: Mechanical, °C 880
1020
Melting Completion (Liquidus), °C 1440
1450
Melting Onset (Solidus), °C 1400
1400
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 25
15
Thermal Expansion, µm/m-K 10
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 3.4
2.3

Otherwise Unclassified Properties

Base Metal Price, % relative 9.0
20
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 2.3
4.1
Embodied Energy, MJ/kg 32
56
Embodied Water, L/kg 120
160

Common Calculations

PREN (Pitting Resistance) 18
31
Resilience: Ultimate (Unit Rupture Work), MJ/m3 88
130
Resilience: Unit (Modulus of Resilience), kJ/m3 130
190
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 15
20
Strength to Weight: Bending, points 16
20
Thermal Diffusivity, mm2/s 6.7
4.1
Thermal Shock Resistance, points 14
13

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 16 to 19
18 to 21
Iron (Fe), % 77.9 to 83.9
58.9 to 70
Manganese (Mn), % 0 to 1.0
0 to 1.5
Molybdenum (Mo), % 0
3.0 to 4.0
Nickel (Ni), % 0
9.0 to 13
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.5
Sulfur (S), % 0 to 0.030
0 to 0.040
Titanium (Ti), % 0.1 to 1.0
0