S44330 Stainless Steel vs. AWS ER100S-1

Both S44330 stainless steel and AWS ER100S-1 are iron alloys. They have 77% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is S44330 stainless steel and the bottom bar is AWS ER100S-1.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 25
18
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 78
73
Tensile Strength: Ultimate (UTS), MPa 440
770
Tensile Strength: Yield (Proof), MPa 230
700

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1390
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 21
49
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.7
7.7
Electrical Conductivity: Equal Weight (Specific), % IACS 3.1
8.9

Otherwise Unclassified Properties

Base Metal Price, % relative 13
3.6
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.8
1.8
Embodied Energy, MJ/kg 40
24
Embodied Water, L/kg 140
54

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 91
130
Resilience: Unit (Modulus of Resilience), kJ/m3 140
1290
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 16
27
Strength to Weight: Bending, points 17
24
Thermal Diffusivity, mm2/s 5.7
13
Thermal Shock Resistance, points 16
23

Alloy Composition

Aluminum (Al), % 0
0 to 0.1
Carbon (C), % 0 to 0.025
0 to 0.080
Chromium (Cr), % 20 to 23
0 to 0.3
Copper (Cu), % 0.3 to 0.8
0 to 0.25
Iron (Fe), % 72.5 to 79.7
93.5 to 96.9
Manganese (Mn), % 0 to 1.0
1.3 to 1.8
Molybdenum (Mo), % 0
0.25 to 0.55
Nickel (Ni), % 0
1.4 to 2.1
Niobium (Nb), % 0 to 0.8
0
Nitrogen (N), % 0 to 0.025
0
Phosphorus (P), % 0 to 0.040
0 to 0.010
Silicon (Si), % 0 to 1.0
0.2 to 0.55
Sulfur (S), % 0 to 0.030
0 to 0.010
Titanium (Ti), % 0 to 0.8
0 to 0.1
Vanadium (V), % 0
0 to 0.050
Zirconium (Zr), % 0
0 to 0.1
Residuals, % 0
0 to 0.5