S44330 Stainless Steel vs. EN 1.0449 Cast Steel

Both S44330 stainless steel and EN 1.0449 cast steel are iron alloys. They have 77% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is S44330 stainless steel and the bottom bar is EN 1.0449 cast steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 25
28
Fatigue Strength, MPa 160
170
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 78
73
Tensile Strength: Ultimate (UTS), MPa 440
460
Tensile Strength: Yield (Proof), MPa 230
220

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 990
400
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 21
52
Thermal Expansion, µm/m-K 10
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.7
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 3.1
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 13
1.8
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.8
1.4
Embodied Energy, MJ/kg 40
18
Embodied Water, L/kg 140
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 91
110
Resilience: Unit (Modulus of Resilience), kJ/m3 140
130
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 16
16
Strength to Weight: Bending, points 17
17
Thermal Diffusivity, mm2/s 5.7
14
Thermal Shock Resistance, points 16
14

Alloy Composition

Carbon (C), % 0 to 0.025
0 to 0.18
Chromium (Cr), % 20 to 23
0
Copper (Cu), % 0.3 to 0.8
0
Iron (Fe), % 72.5 to 79.7
98 to 100
Manganese (Mn), % 0 to 1.0
0 to 1.2
Niobium (Nb), % 0 to 0.8
0
Nitrogen (N), % 0 to 0.025
0
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 0.6
Sulfur (S), % 0 to 0.030
0 to 0.025
Titanium (Ti), % 0 to 0.8
0