S44537 Stainless Steel vs. S35140 Stainless Steel
Both S44537 stainless steel and S35140 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 71% of their average alloy composition in common.
For each property being compared, the top bar is S44537 stainless steel and the bottom bar is S35140 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 180 | |
| 210 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 200 |
| Elongation at Break, % | 21 | |
| 34 |
| Fatigue Strength, MPa | 230 | |
| 250 |
| Poisson's Ratio | 0.27 | |
| 0.28 |
| Rockwell B Hardness | 80 | |
| 88 |
| Shear Modulus, GPa | 79 | |
| 78 |
| Shear Strength, MPa | 320 | |
| 460 |
| Tensile Strength: Ultimate (UTS), MPa | 510 | |
| 690 |
| Tensile Strength: Yield (Proof), MPa | 360 | |
| 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 300 |
| Maximum Temperature: Corrosion, °C | 530 | |
| 500 |
| Maximum Temperature: Mechanical, °C | 1000 | |
| 1100 |
| Melting Completion (Liquidus), °C | 1480 | |
| 1420 |
| Melting Onset (Solidus), °C | 1430 | |
| 1370 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 21 | |
| 14 |
| Thermal Expansion, µm/m-K | 11 | |
| 16 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.6 | |
| 1.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.0 | |
| 1.9 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 19 | |
| 31 |
| Density, g/cm3 | 7.9 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 3.4 | |
| 5.5 |
| Embodied Energy, MJ/kg | 50 | |
| 78 |
| Embodied Water, L/kg | 140 | |
| 190 |
Common Calculations
| PREN (Pitting Resistance) | 26 | |
| 28 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 95 | |
| 190 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 320 | |
| 250 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 18 | |
| 24 |
| Strength to Weight: Bending, points | 18 | |
| 22 |
| Thermal Diffusivity, mm2/s | 5.6 | |
| 3.7 |
| Thermal Shock Resistance, points | 17 | |
| 16 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.1 | |
| 0 |
| Carbon (C), % | 0 to 0.030 | |
| 0 to 0.1 |
| Chromium (Cr), % | 20 to 24 | |
| 20 to 22 |
| Copper (Cu), % | 0 to 0.5 | |
| 0 |
| Iron (Fe), % | 69 to 78.6 | |
| 44.1 to 52.7 |
| Lanthanum (La), % | 0.040 to 0.2 | |
| 0 |
| Manganese (Mn), % | 0 to 0.8 | |
| 1.0 to 3.0 |
| Molybdenum (Mo), % | 0 | |
| 1.0 to 2.0 |
| Nickel (Ni), % | 0 to 0.5 | |
| 25 to 27 |
| Niobium (Nb), % | 0.2 to 1.0 | |
| 0.25 to 0.75 |
| Nitrogen (N), % | 0 to 0.040 | |
| 0.080 to 0.2 |
| Phosphorus (P), % | 0 to 0.050 | |
| 0 to 0.045 |
| Silicon (Si), % | 0.1 to 0.6 | |
| 0 to 0.75 |
| Sulfur (S), % | 0 to 0.0060 | |
| 0 to 0.030 |
| Titanium (Ti), % | 0.020 to 0.2 | |
| 0 |
| Tungsten (W), % | 1.0 to 3.0 | |
| 0 |