S44626 Stainless Steel vs. EN 1.6750 Steel

Both S44626 stainless steel and EN 1.6750 steel are iron alloys. They have 73% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is S44626 stainless steel and the bottom bar is EN 1.6750 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
190
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 23
18
Fatigue Strength, MPa 230
310
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 80
73
Tensile Strength: Ultimate (UTS), MPa 540
650
Tensile Strength: Yield (Proof), MPa 350
460

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1100
420
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 17
39
Thermal Expansion, µm/m-K 11
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 14
3.3
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 2.9
1.7
Embodied Energy, MJ/kg 42
22
Embodied Water, L/kg 160
52

Common Calculations

PREN (Pitting Resistance) 30
2.4
Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
110
Resilience: Unit (Modulus of Resilience), kJ/m3 300
570
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 26
24
Strength to Weight: Axial, points 19
23
Strength to Weight: Bending, points 19
21
Thermal Diffusivity, mm2/s 4.6
10
Thermal Shock Resistance, points 18
19

Alloy Composition

Carbon (C), % 0 to 0.060
0.17 to 0.23
Chromium (Cr), % 25 to 27
0.3 to 0.5
Copper (Cu), % 0 to 0.2
0
Iron (Fe), % 68.1 to 74.1
95.3 to 97.5
Manganese (Mn), % 0 to 0.75
0.8 to 1.2
Molybdenum (Mo), % 0.75 to 1.5
0.4 to 0.8
Nickel (Ni), % 0 to 0.5
0.8 to 1.2
Nitrogen (N), % 0 to 0.040
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 0.75
0 to 0.6
Sulfur (S), % 0 to 0.020
0 to 0.030
Titanium (Ti), % 0.2 to 1.0
0