S44626 Stainless Steel vs. S35135 Stainless Steel

Both S44626 stainless steel and S35135 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 62% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is S44626 stainless steel and the bottom bar is S35135 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 23
34
Fatigue Strength, MPa 230
180
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 80
79
Shear Strength, MPa 340
390
Tensile Strength: Ultimate (UTS), MPa 540
590
Tensile Strength: Yield (Proof), MPa 350
230

Thermal Properties

Latent Heat of Fusion, J/g 300
320
Maximum Temperature: Corrosion, °C 560
560
Maximum Temperature: Mechanical, °C 1100
1100
Melting Completion (Liquidus), °C 1440
1430
Melting Onset (Solidus), °C 1390
1380
Specific Heat Capacity, J/kg-K 480
470
Thermal Expansion, µm/m-K 11
16

Otherwise Unclassified Properties

Base Metal Price, % relative 14
37
Density, g/cm3 7.7
8.1
Embodied Carbon, kg CO2/kg material 2.9
6.8
Embodied Energy, MJ/kg 42
94
Embodied Water, L/kg 160
220

Common Calculations

PREN (Pitting Resistance) 30
37
Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
160
Resilience: Unit (Modulus of Resilience), kJ/m3 300
130
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 26
24
Strength to Weight: Axial, points 19
20
Strength to Weight: Bending, points 19
19
Thermal Shock Resistance, points 18
13

Alloy Composition

Carbon (C), % 0 to 0.060
0 to 0.080
Chromium (Cr), % 25 to 27
20 to 25
Copper (Cu), % 0 to 0.2
0 to 0.75
Iron (Fe), % 68.1 to 74.1
28.3 to 45
Manganese (Mn), % 0 to 0.75
0 to 1.0
Molybdenum (Mo), % 0.75 to 1.5
4.0 to 4.8
Nickel (Ni), % 0 to 0.5
30 to 38
Nitrogen (N), % 0 to 0.040
0
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 0.75
0.6 to 1.0
Sulfur (S), % 0 to 0.020
0 to 0.015
Titanium (Ti), % 0.2 to 1.0
0.4 to 1.0