S44627 Stainless Steel vs. EN 1.8965 Steel

Both S44627 stainless steel and EN 1.8965 steel are iron alloys. They have 73% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is S44627 stainless steel and the bottom bar is EN 1.8965 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
170
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 24
16
Fatigue Strength, MPa 200
220
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 80
73
Shear Strength, MPa 310
350
Tensile Strength: Ultimate (UTS), MPa 490
570
Tensile Strength: Yield (Proof), MPa 300
340

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 1100
420
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 17
39
Thermal Expansion, µm/m-K 11
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 14
3.0
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.9
1.8
Embodied Energy, MJ/kg 41
25
Embodied Water, L/kg 160
52

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
78
Resilience: Unit (Modulus of Resilience), kJ/m3 220
300
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 18
20
Strength to Weight: Bending, points 18
19
Thermal Diffusivity, mm2/s 4.6
10
Thermal Shock Resistance, points 16
17

Alloy Composition

Aluminum (Al), % 0
0 to 0.030
Carbon (C), % 0 to 0.010
0 to 0.19
Chromium (Cr), % 25 to 27.5
0.35 to 0.85
Copper (Cu), % 0 to 0.2
0.2 to 0.6
Iron (Fe), % 69.2 to 74.2
94.6 to 99
Manganese (Mn), % 0 to 0.4
0.45 to 1.6
Molybdenum (Mo), % 0.75 to 1.5
0 to 0.35
Nickel (Ni), % 0 to 0.5
0 to 0.7
Niobium (Nb), % 0.050 to 0.2
0 to 0.065
Nitrogen (N), % 0 to 0.015
0
Phosphorus (P), % 0 to 0.020
0 to 0.035
Silicon (Si), % 0 to 0.4
0 to 0.55
Sulfur (S), % 0 to 0.020
0 to 0.035
Titanium (Ti), % 0
0 to 0.12
Vanadium (V), % 0
0 to 0.14
Zirconium (Zr), % 0
0 to 0.17