S44660 Stainless Steel vs. EN 1.4513 Stainless Steel

Both S44660 stainless steel and EN 1.4513 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 85% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is S44660 stainless steel and the bottom bar is EN 1.4513 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
200
Elongation at Break, % 20
26
Fatigue Strength, MPa 330
170
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 81
77
Shear Strength, MPa 410
310
Tensile Strength: Ultimate (UTS), MPa 660
480
Tensile Strength: Yield (Proof), MPa 510
240

Thermal Properties

Latent Heat of Fusion, J/g 300
280
Maximum Temperature: Corrosion, °C 640
500
Maximum Temperature: Mechanical, °C 1100
880
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1410
1410
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 17
25
Thermal Expansion, µm/m-K 11
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.5
2.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.9
2.9

Otherwise Unclassified Properties

Base Metal Price, % relative 21
10
Density, g/cm3 7.7
7.7
Embodied Carbon, kg CO2/kg material 4.3
2.5
Embodied Energy, MJ/kg 61
35
Embodied Water, L/kg 180
120

Common Calculations

PREN (Pitting Resistance) 38
21
Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
100
Resilience: Unit (Modulus of Resilience), kJ/m3 640
150
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 24
17
Strength to Weight: Bending, points 22
18
Thermal Diffusivity, mm2/s 4.5
6.8
Thermal Shock Resistance, points 21
17

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.025
Chromium (Cr), % 25 to 28
16 to 18
Iron (Fe), % 60.4 to 71
77.7 to 83.1
Manganese (Mn), % 0 to 1.0
0 to 1.0
Molybdenum (Mo), % 3.0 to 4.0
0.8 to 1.4
Nickel (Ni), % 1.0 to 3.5
0
Niobium (Nb), % 0.2 to 1.0
0
Nitrogen (N), % 0 to 0.040
0 to 0.020
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015
Titanium (Ti), % 0.2 to 1.0
0.15 to 0.8