S44700 Stainless Steel vs. EN 1.0425 Steel

Both S44700 stainless steel and EN 1.0425 steel are iron alloys. They have 67% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is S44700 stainless steel and the bottom bar is EN 1.0425 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200
140
Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 23
24
Fatigue Strength, MPa 300
190
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 82
73
Shear Strength, MPa 380
300
Tensile Strength: Ultimate (UTS), MPa 600
470
Tensile Strength: Yield (Proof), MPa 450
260

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1410
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Expansion, µm/m-K 11
12

Otherwise Unclassified Properties

Base Metal Price, % relative 18
2.2
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.6
1.5
Embodied Energy, MJ/kg 49
20
Embodied Water, L/kg 180
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
98
Resilience: Unit (Modulus of Resilience), kJ/m3 480
180
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
17
Strength to Weight: Bending, points 20
17
Thermal Shock Resistance, points 19
15

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.024
Carbon (C), % 0 to 0.010
0 to 0.2
Chromium (Cr), % 28 to 30
0 to 0.3
Copper (Cu), % 0 to 0.15
0 to 0.3
Iron (Fe), % 64.9 to 68.5
96.9 to 99.18
Manganese (Mn), % 0 to 0.3
0.8 to 1.4
Molybdenum (Mo), % 3.5 to 4.2
0 to 0.080
Nickel (Ni), % 0 to 0.15
0 to 0.3
Niobium (Nb), % 0
0 to 0.020
Nitrogen (N), % 0 to 0.020
0 to 0.012
Phosphorus (P), % 0 to 0.025
0 to 0.025
Silicon (Si), % 0 to 0.2
0 to 0.4
Sulfur (S), % 0 to 0.020
0 to 0.010
Titanium (Ti), % 0
0 to 0.030
Vanadium (V), % 0
0 to 0.020