S44700 Stainless Steel vs. EN 1.4552 Stainless Steel

Both S44700 stainless steel and EN 1.4552 stainless steel are iron alloys. They have 86% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is S44700 stainless steel and the bottom bar is EN 1.4552 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200
150
Elastic (Young's, Tensile) Modulus, GPa 210
200
Elongation at Break, % 23
29
Fatigue Strength, MPa 300
150
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 82
77
Tensile Strength: Ultimate (UTS), MPa 600
510
Tensile Strength: Yield (Proof), MPa 450
200

Thermal Properties

Latent Heat of Fusion, J/g 300
290
Maximum Temperature: Corrosion, °C 460
490
Maximum Temperature: Mechanical, °C 1100
960
Melting Completion (Liquidus), °C 1460
1430
Melting Onset (Solidus), °C 1410
1380
Specific Heat Capacity, J/kg-K 480
480
Thermal Expansion, µm/m-K 11
17

Otherwise Unclassified Properties

Base Metal Price, % relative 18
19
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.6
3.6
Embodied Energy, MJ/kg 49
52
Embodied Water, L/kg 180
150

Common Calculations

PREN (Pitting Resistance) 42
19
Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
120
Resilience: Unit (Modulus of Resilience), kJ/m3 480
100
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21
18
Strength to Weight: Bending, points 20
18
Thermal Shock Resistance, points 19
11

Alloy Composition

Carbon (C), % 0 to 0.010
0 to 0.070
Chromium (Cr), % 28 to 30
18 to 20
Copper (Cu), % 0 to 0.15
0
Iron (Fe), % 64.9 to 68.5
63.9 to 73
Manganese (Mn), % 0 to 0.3
0 to 1.5
Molybdenum (Mo), % 3.5 to 4.2
0
Nickel (Ni), % 0 to 0.15
9.0 to 12
Niobium (Nb), % 0
0 to 1.0
Nitrogen (N), % 0 to 0.020
0
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.2
0 to 1.5
Sulfur (S), % 0 to 0.020
0 to 0.030