MakeItFrom.com
Menu (ESC)

S44700 Stainless Steel vs. Grade VDC Steel

Both S44700 stainless steel and grade VDC steel are iron alloys. They have 67% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is S44700 stainless steel and the bottom bar is grade VDC steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200
510
Elastic (Young's, Tensile) Modulus, GPa 210
190
Poisson's Ratio 0.27
0.29
Reduction in Area, % 45
50
Shear Modulus, GPa 82
80
Tensile Strength: Ultimate (UTS), MPa 600
1700

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1410
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Expansion, µm/m-K 11
13

Otherwise Unclassified Properties

Base Metal Price, % relative 18
1.9
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.6
1.4
Embodied Energy, MJ/kg 49
19
Embodied Water, L/kg 180
47

Common Calculations

Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
60
Strength to Weight: Bending, points 20
40
Thermal Shock Resistance, points 19
50

Alloy Composition

Carbon (C), % 0 to 0.010
0.6 to 0.75
Chromium (Cr), % 28 to 30
0 to 0.3
Copper (Cu), % 0 to 0.15
0 to 0.060
Iron (Fe), % 64.9 to 68.5
98.3 to 99.35
Manganese (Mn), % 0 to 0.3
0.5 to 1.0
Molybdenum (Mo), % 3.5 to 4.2
0
Nickel (Ni), % 0 to 0.15
0
Nitrogen (N), % 0 to 0.020
0
Phosphorus (P), % 0 to 0.025
0 to 0.020
Silicon (Si), % 0 to 0.2
0.15 to 0.3
Sulfur (S), % 0 to 0.020
0 to 0.020